SP-04 is a two-pack, seamless, epoxy floor coating system with the following properties:

  Excellent decorating effect.

  Mixed color freely.

  Excellent abrasion resistance.

  Good corrosion resistance against acids, alkalis resistance.

  Very high mechanical strength.

  High level of aesthetics:

 SP-04 is mainly suitable for places where, for ergonomic reason, the above properties are required in office, subway, airdrome, multipurpose hall, exhibition hall, apartment, hotel, dining room, rest area, hospital, school, etc.

Packing

 SP-04 Part A: 15kg containers.

 SP-04 Part B: 15kg containers

SP-04 Epoxy colorful silica floor coating system
Product description
SP-04 is a two-pack, seamless, epoxy floor coating system with the following
properties.
l Excellent decorating effect.
l Mixed color freely.
l Excellent abrasion resistance.
l Good corrosion resistance against acids, alkalis resistance.
l Very high mechanical strength
l High level of aesthetics;
Application areas
SP-04 is specially suitable for places where, for ergonomic reason, the above
properties are required in an office, subway, airdrome, multipurpose hall, exhibition hall,
apartment, hotel, dining room, rest area, hospital, school, etc.
Performance data
ITEM INDEX
Touch dry ≤6
Drying time,h:
Hard dry ≤24
Abrasion esistance(1000g/1000r,weight loss,g) ≤0.03.
Compressive strength, Mpa ≥70
Flexible strength, Mpa ≥6.
Tensile strength, Mpa ≥7.
Bonding strength, Mpa ≥2
Shore D hardness ≥80.
Application instructions
Surface preparation
l The compressive strength of the concrete substrate should not be less than 25N/mm2,
the best application temperature is between 10--25.The air humidity must not be
higher than 80%, the moisture content of the substrate shall not be higher than 8.
l Correct substrate preparation is critical for optimum performance. Surfaces should be
sound, clean, dry and free from loose particles, oil, grease, and all other
contaminants
l Remove oil, grease by scrubbing. Cement laitance, loose particles, pitch and other
contaminants must be removed from the surface by sand-blasting. The alkalinity and
porosity of the surface must also be considered when painting.
l Fill surface cracks with epoxy-reinforced solvent-free repair mortar to achieve a level
surface.