Detailed Product Description

     SP-08 is a self-leveling epoxy flooring system with the following  properties:

  Excellent anti-electrostatic property.

  Excellent chemical and abrasion resistance.

  Seamless and glossy.

  Excellent resistance to corrosion and cracking properties.

Application areas

SP-08 is mainly recommended for floor in environments where static electricity and stray currents produced by friction or the production of electronic parts. It is recommended for floors in:

  Electronic industries.

  Wafer and PC component production.

  Synthetic fiber mills.

Packing and colours

 SP-08 Part A: 15kg containers.

 SP-08 Part B: 15kg containers.

 SP-08 is available in large range of colors. For available colors, please refer to color chart.

SP-08 Anti-static self-leveling epoxy floor coating system
Product description
SP-08 is a self-leveling epoxy flooring system with the following properties:
l Excellent anti-electrostatic property.
l Excellent chemical and abrasion resistance.
l Seamless and glossy.
l Excellent resistance to corrosion and cracking.
SP-08 is available in a large range of colors. For available colors, please refer to color
chart.
Application areas
SP-08 is mainly recommended for floors in environments where static electricity and
stray currents are produced by friction or the production of electronic parts. It is
recommended for floors in
l Electronic industries;
l Wafer and PC component production;
l Synthetic fiber mills.
Performance data

ITEM INDEX
Touch dry ≤ 4h,
Drying time,h
Hard dry ≤ 24h.
Solid by weigh : 90
Surface resistance 106-109
Volume resistance 106-109
Shore D hardness ≥70
Tensile strength MPa 9
Flexible strength Mpa 7
Compressive strength Mpa 85
Bonding strength MPa ≥2
Abrasion resistance,750g/500r, weight loss, g: ≤ 0.02
Anti-60sulfuric acid Permit little color changed in 30 days.
Anti-30salt water : No change in 30 days.
Anti-25% sodium hydroxide: No change in 30days.
Anti-petrol, 120#: No change in 56 days

Application instructions
Surface preparation
l The compressive strength of the concrete substrate should not be less than 25N/mm2,
the best application temperature is between 10--25.The air humidity must not be
higher than 80%, the moisture content of the substrate shall not be higher than 8.
l Correct substrate preparation is critical for optimum performance. Surfaces should be sound, clean, dry and free from loose particles, oil, grease, and all other contaminants
l Remove oil, grease by scrubbing. Cement laitance, loose particles, pitch and other
contaminants must be removed from the surface by sand-blasting. The alkalinity and
porosity of the surface must also be considered when painting.
l Fill surface cracks with Epoxy-Reinforced Solvent-Free repair mortar to achieve a
level surface.